- •Pulp Purification Herbert Sixta
- •9.2.2.1 Introduction
- •Introduction
- •10.4 Emissions to the Aquatic Environment
- •Is converted into carbon dioxide, while the other half is converted into biomass
- •Into alcohols and aldehydes; (c) conversion of these intermediates into acetic acid and
- •10 Environmental Aspects of Pulp Production
- •In North America, effluent color is a parameter which must be monitored.
- •It is not contaminated with other trace elements such as mercury, lead, or cadmium.
- •10.6 Outlook
- •Increase pollution by causing a higher demand for a chemical to achieve identical
- •In addition negatively affect fiber strength, which in turn triggers a higher
- •Introduction
- •2002, Paper-grade pulp accounts for almost 98% of the total wood pulp production
- •Important pulping method until the 1930s) continuously loses ground and finds
- •Importance in newsprint has been declining in recent years with the increasing
- •Isbn: 3-527-30999-3
- •Virtually all paper and paperboard grades in order to improve strength properties.
- •In fact, the word kraft is the Swedish and German word for strength. Unbleached
- •Importance is in the printing and writing grades. In these grades, softwood
- •In this chapter, the main emphasis is placed on a comprehensive discussion of
- •1010 11 Pulp Properties and Applications
- •Is particularly sensitive to alkaline cleavage. The decrease in uronic acid content
- •Xylan in the surface layers of kraft pulps as compared to sulfite pulps has been
- •80% Cellulose content the fiber strength greatly diminishes [14]. This may be due
- •Viscoelastic and capable of absorbing more energy under mechanical stress. The
- •11.2 Paper-Grade Pulp 1011
- •Various pulping treatments using black spruce with low fibril
- •In the viscoelastic regions. Fibers of high modulus and elasticity tend to peel their
- •1012 11 Pulp Properties and Applications
- •11.2 Paper-Grade Pulp
- •Viscosity mL g–1 793 635 833 802 1020 868 1123
- •Xylose % od pulp 7.3 6.9 18.4 25.5 4.1 2.7 12.2
- •11 Pulp Properties and Applications
- •Inorganic Compounds
- •11.2 Paper-Grade Pulp
- •Insight into many aspects of pulp origin and properties, including the type of
- •Indicate oxidative damage of carbohydrates).
- •In general, the r-values of paper pulps are typically at higher levels as predicted
- •Is true for sulfite pulps. Even though the r-values of sulfite pulps are generally
- •Is rather unstable in acid sulfite pulping, and this results in a low (hemicellulose)
- •11 Pulp Properties and Applications
- •Ing process, for example the kraft process, the cellulose:hemicellulose ratio is
- •Increases by up to 100%. In contrast to fiber strength, the sheet strength is highly
- •Identified as the major influencing parameter of sheet strength properties. It has
- •In contrast to dissolving pulp specification, the standard characterization of
- •Is observed for beech kraft pulp, which seems to correlate with the enhanced
- •11.2 Paper-Grade Pulp
- •11 Pulp Properties and Applications
- •Is significantly higher for the sulfite as compared to the kraft pulps, and indicates
- •11.2 Paper-Grade Pulp
- •Xylan [24].
- •11 Pulp Properties and Applications
- •11.2 Paper-Grade Pulp
- •11 Pulp Properties and Applications
- •Introduction
- •Various cellulose-derived products such as regenerated fibers or films (e.G.,
- •Viscose, Lyocell), cellulose esters (acetates, propionates, butyrates, nitrates) and
- •In pulping and bleaching operations are required in order to obtain a highquality
- •Important pioneer of cellulose chemistry and technology, by the statement that
- •11.3 Dissolving Grade Pulp
- •Involves the extensive characterization of the cellulose structure at three different
- •Is an important characteristic of dissolving pulps. Finally, the qualitative and
- •Inorganic compounds
- •11 Pulp Properties and Applications
- •11.3.2.1 Pulp Origin, Pulp Consumers
- •Include the recently evaluated Formacell procedure [7], as well as the prehydrolysis-
- •11.3 Dissolving Grade Pulp
- •Viscose
- •11 Pulp Properties and Applications
- •11.3.2.2 Chemical Properties
- •11.3.2.2.1 Chemical Composition
- •In the polymer. The available purification processes – particularly the hot and cold
- •11.3 Dissolving Grade Pulp
- •In the steeping lye inhibits cellulose degradation during ageing due to the
- •Is governed by a low content of noncellulosic impurities, particularly pentosans,
- •Increase in the xylan content in the respective viscose fibers clearly support the
- •11.3 Dissolving Grade Pulp
- •Instability. Diacetate color is measured by determining the yellowness coefficient
- •Xylan content [%]
- •11 Pulp Properties and Applications
- •Xylan content [%]
- •11.3 Dissolving Grade Pulp
- •11.3 Dissolving Grade Pulp
- •Is, however, not the only factor determining the optical properties of cellulosic
- •In the case of alkaline derivatization procedures (e.G., viscose, ethers). In industrial
- •11.3 Dissolving Grade Pulp
- •Viscose
- •Viscose
- •In order to bring out the effect of mwd on the strength properties of viscose
- •Imitating the regular production of rayon fibers. To obtain a representative view
- •11 Pulp Properties and Applications
- •Viscose Ether (hv) Viscose Acetate Acetate
- •Xylan % 3.6 3.1 1.5 0.9 0.2
- •1.3 Dtex regular viscose fibers in the conditioned
- •11.3 Dissolving Grade Pulp
- •Is more pronounced for sulfite than for phk pulps. Surprisingly, a clear correlation
- •Viscose fibers in the conditioned state related to the carbonyl
- •1038 11 Pulp Properties and Applications
- •In a comprehensive study, the effect of placing ozonation before (z-p) and after
- •Increased from 22.9 to 38.4 lmol g–1 in the case of a pz-sequence, whereas
- •22.3 To 24.2 lmol g–1. The courses of viscosity and carboxyl group contents were
- •Viscosity measurement additionally induces depolymerization due to strong
- •11 Pulp Properties and Applications
- •Increasing ozone charges. For more detailed
- •11.3 Dissolving Grade Pulp
- •Is more selective when ozonation represents the final stage according to an
- •11.3.2.3 Supramolecular Structure
- •1042 11 Pulp Properties and Applications
- •Is further altered by subsequent bleaching and purification processes. This
- •Involved in intra- and intermolecular hydrogen bonds. The softened state favors
- •11.3 Dissolving Grade Pulp
- •Interestingly, the resistance to mercerization, which refers to the concentration of
- •11 Pulp Properties and Applications
- •Illustrate that the difference in lye concentration between the two types of dissolving
- •Intensity (see Fig. 11.18: hw-phk high p-factor) clearly changes the supramolecular
- •11.3 Dissolving Grade Pulp
- •Viscose filterability, thus indicating an improved reactivity.
- •11 Pulp Properties and Applications
- •Impairs the accessibility of the acetylation agent. When subjecting a low-grade dissolving
- •Identification of the cell wall layers is possible by the preferred orientation of
- •Viscose pulp (low p-factor) (Fig. 11.21b, top). Apparently, the type of pulp – as well
- •11 Pulp Properties and Applications
- •150 °C for 2 h, more than 70% of a xylan, which was added to the cooking liquor
- •20% In the case of alkali concentrations up to 50 g l–1 [67]. Xylan redeposition has
- •11.3 Dissolving Grade Pulp
- •Xylan added linters cooked without xylan linters cooked with xylan
- •Viscosity
- •In the surface layer than in the inner fiber wall. This is in agreement with
- •11 Pulp Properties and Applications
- •Xylan content in peelings [wt%]
- •Xylan content located in the outermost layers of the beech phk fibers suggests
- •11.3.2.5 Fiber Morphology
- •11 Pulp Properties and Applications
- •50 And 90%. Moreover, bleachability of the screened pulps from which the wood
- •11.3.2.6 Pore Structure, Accessibility
- •11.3 Dissolving Grade Pulp
- •Volume (Vp), wrv and specific pore surface (Op) were seen between acid sulfite
- •11 Pulp Properties and Applications
- •Irreversible loss of fiber swelling occurs; indeed, Maloney and Paulapuro reported
- •In microcrystalline areas as the main reason for hornification [85]. The effect of
- •105 °C, thermal degradation proceeds in parallel with hornification, as shown in
- •Increased, particularly at temperatures above 105 °c. The increase in carbonyl
- •In pore volume is clearly illustrated in Fig. 11.28.
- •11.3 Dissolving Grade Pulp
- •Viscosity
- •11 Pulp Properties and Applications
- •Increase in the yellowness coefficient, haze, and the amount of undissolved particles.
- •11.3.2.7 Degradation of Dissolving Pulps
- •In mwd. A comprehensive description of all relevant cellulose degradation processes
- •Is reviewed in Ref. [4]. The different modes of cellulose degradation comprise
- •11.3 Dissolving Grade Pulp
- •50 °C, is illustrated graphically in Fig. 11.29.
- •11 Pulp Properties and Applications
- •In the crystalline regions.
- •11.3 Dissolving Grade Pulp
- •Important dissolving pulps, derived from hardwood, softwood and cotton linters
- •11.3 Dissolving Grade Pulp 1061
- •Xylan rel% ax/ec-pad 2.5 3.5 1.3 1.0 3.2 0.4
- •Viscosity mL g–1 scan-cm 15:99 500 450 820 730 1500 2000
- •1062 11 Pulp Properties and Applications
Xylan [24].
However, sheet properties are determined by many other parameters such as
the cellulose:hemicellulose ratio, as previously discussed. Another important factor
for pulp sheet properties is fiber morphology, characterized by fiber length,
fiber length distribution, and coarseness. It is widely accepted that especially
1019
11 Pulp Properties and Applications
2 4 6 8
0
100
120
140
160
Zero-Span tensile index, dry [Nm/g]
Weight fraction < DP 120
Fig. 11.4 Relationship between zero-span tensile index and
the weight fraction <DP 120 of a representative selection of
commercial hardwood and softwood kraft and sulfite pulps
[17]. For more detailed information on these pulps, see
Tabs. 11.1 and 11.2.
tearing strength is influenced by fiber length. Based on the comparison between
hardwood and softwood kraft pulps, the poorer tearing strength of the former is
generally attributed to the shorter fiber length. The results of the measurement of
the fiber dimensions of the selected paper pulps are provided in Fig. 11.5 and
Tab. 11.3.
By comparing the fiber length distribution of both spruce pulps, it is apparent
that the sulfite pulp shows a higher proportion of short fibers as compared to the
kraft pulp. This may be attributed to the degraded cellulose fraction formed during
the late stage of cooking. The beech pulp shows the characteristic peak at a
fiber length below 0.2 mm, indicating the presence of large amounts of fines derived
by both parenchymal cells (primary fines) and degraded pulp fibers (secondary
fines). In contrast, eucalyptus pulps are characteristic for a narrow fiber length
distribution and an extremely low coarseness which contributes to a high accessible
surface area of the pulp fibers.
1020
11.2 Paper-Grade Pulp
0 1 2 3 4 5 6
Spruce-KRAFT
Fiber Length [mm]
Spruce-SULFITE
Eucalyptus-KRAFT
Lenght weighted fraction [%]
Beech-SULFITE
Fig. 11.5 Fiber dimensions of a representative selection of
commercial hardwood and softwood kraft and sulfite pulps
[17]. Fiber dimensions determined using Kajaani FS200.
Tab. 11.3 Fiber dimensions of fully bleached commercial paper
pulps, as determined with Kajaani FS200 [17].
Parameter Pine Spruce Eucalyptus Beech Spruce Spruce Beech
Kraft Kraft Sulfite Sulfite
ECF TCF ECF ECF TCF ECF TCF
Average fiber length
arithmetic mm 0.90 1.04 0.55 n.d. 0.79 0.52 0.28
length-weighted mm 2.16 2.36 0.72 n.d. 2.15 1.89 0.66
weight-weighted mm 2.82 3.01 0.91 n.d. 2.93 2.91 0.86
Fines (P < 0.2 mm) wt% 3.5 2.7 2.0 n.d. 4.2 7.9 12.8
Coarseness mg m–1 0.213 0.215 0.074 n.d. 0.227 0.219 0.122
n.d. = not determined
1021
11 Pulp Properties and Applications
11.3
Dissolving Grade Pulp
11.3.1
Introduction
Dissolving pulp refers to pulp of high cellulose content which is used to manufacture
Various cellulose-derived products such as regenerated fibers or films (e.G.,
Viscose, Lyocell), cellulose esters (acetates, propionates, butyrates, nitrates) and
cellulose ethers (carboxymethyl-, ethyl-, methyl-celluloses). The wood-derived celluloses
which account for about 85–88% of the total dissolving pulp market are
made by the prehydrolysis kraft and acid sulfite processes comprising additional
purification stages such as hot and cold caustic extraction. The residual amount of
dissolving pulps is based on cotton linters. The linters fibers, being attached to
the cotton seeds, are removed by the delintering process, producing fibers of different
lengths. The shortest fibers or second-cut linters are used as chemical feedstock.
Purification is accomplished by a combination of mechanical and chemical
steps comprising mild alkali treatment at elevated temperature to remove proteins,
waxes, pectins and other polysaccharides and bleaching to achieve the required
brightness level. Purified cotton linters represent the dissolving pulp of
highest cellulose purity particularly used for manufacturing acetate plastics and
high-viscosity cellulose ethers.
When using softwoods and hardwoods as a raw material, more drastic conditions